TEIJIN® TETORON® G2

Product Description

Teijin® Teroron® G2 is a polyester film which has high clarity and good slip characteristics.

Special Features

Teijin® Tetoron® G2 is available in the following variations: G2: Non-pretreated G2N: Adhesion Pretreated (one side) G2C: Corona Treated (one side) G2Z: Release Pretreated (one side) Note: Two different shrinkage versions are available in 65* and 80* gauge (as reported in Property Table)

Typical Applications

Teijin® Tetoron® G2 is suitable for applications where low haze and good handling are desired product qualities. Intended applications include: Labels Release Films Holograms Dry Film Resist (DFR)

Typical Properties

Available Thickness [Gauge] 65;    75;    80;    92;    100;    150;    200

Property Thickness Value Units Test OPTICAL Haze  100  2.4  %  ASTM D1003  Haze  150  2.9  %  ASTM D1003  Haze  200  4.5  %  ASTM D1003  Haze  65  2.0 (2.1*)  %  ASTM D1003  Haze  75  2.2  %  ASTM D1003  Haze  80  2.2 (2.3*)  %  ASTM D1003  Haze  92  2.5  %  ASTM D1003    PHYSICAL C.O.F. (dynamic)  100  0.35    ASTM D1894  C.O.F. (dynamic)  150  0.34    ASTM D1894  C.O.F. (dynamic)  200  0.30    ASTM D1894  C.O.F. (dynamic)  75  0.35    ASTM D1894  C.O.F. (dynamic)  92  0.35    ASTM D1894  C.O.F. (static)  100  0.43    ASTM D1894  C.O.F. (static)  150  0.44    ASTM D1894  C.O.F. (static)  200  0.30    ASTM D1894  C.O.F. (static)  75  0.41    ASTM D1894  C.O.F. (static)  92  0.41    ASTM D1894  Elongation at Break MD  100  120  %  ASTM D882A  Elongation at Break MD  150  130  %  ASTM D882A  Elongation at Break MD  200  130  %  ASTM D882A  Elongation at Break MD  65  150 (140*)  %  ASTM D882A  Elongation at Break MD  75  150  %  ASTM D882A  Elongation at Break MD  80  150 (140*)  %  ASTM D882A  Elongation at Break MD  92  150  %  ASTM D882A  Elongation at Break TD  100  110  %  ASTM D882A  Elongation at Break TD  150  120  %  ASTM D882A  Elongation at Break TD  200  110  %  ASTM D882A  Elongation at Break TD  65  100 (100*)  %  ASTM D882A  Elongation at Break TD  75  100  %  ASTM D882A  Elongation at Break TD  80  100 (100*)  %  ASTM D882A  Elongation at Break TD  92  110  %  ASTM D882A  Tensile Strength MD  100  38,425  psi  ASTM D882A  Tensile Strength MD  150  41,180  psi  ASTM D882A  Tensile Strength MD  200  39,730  psi  ASTM D882A  Tensile Strength MD  65  36,975  psi  ASTM D882A  Tensile Strength MD  75  35,525  psi  ASTM D882A  Tensile Strength MD  80  36,975  psi  ASTM D882A  Tensile Strength MD  92  36,975  psi  ASTM D882A  Tensile Strength TD  100  42,630  psi  ASTM D882A  Tensile Strength TD  150  42,630  psi  ASTM D882A  Tensile Strength TD  200  38,425  psi  ASTM D882A  Tensile Strength TD  65  45,530  psi  ASTM D882A  Tensile Strength TD  75  44,080  psi  ASTM D882A  Tensile Strength TD  80  44,080  psi  ASTM D882A  Tensile Strength TD  92  44,080  psi  ASTM D882A    THERMAL Shrinkage MD (150°C)  100  1.6  %  Unrestrained @ 150°C/30 min  Shrinkage MD (150°C)  150  1.8  %  Unrestrained @ 150°C/30 min  Shrinkage MD (150°C)  200  1.9  %  Unrestrained @ 150°C/30 min  Shrinkage MD (150°C)  65  1.8 (1.8*)  %  Unrestrained @ 150°C/30 min  Shrinkage MD (150°C)  75  1.7  %  Unrestrained @ 150°C/30 min  Shrinkage MD (150°C)  80  1.7 (1.8*)  %  Unrestrained @ 150°C/30 min  Shrinkage MD (150°C)  92  1.7  %  Unrestrained @ 150°C/30 min  Shrinkage TD (150°C)  100  0.5  %  Unrestrained @ 150°C/30 min  Shrinkage TD (150°C)  150  0.5  %  Unrestrained @ 150°C/30 min  Shrinkage TD (150°C)  200  0.3  %  Unrestrained @ 150°C/30 min  Shrinkage TD (150°C)  65  1.0 (1.7*)  %  Unrestrained @ 150°C/30 min  Shrinkage TD (150°C)  75  0.9  %  Unrestrained @ 150°C/30 min  Shrinkage TD (150°C)  80  0.9 (1.7*)  %  Unrestrained @ 150°C/30 min  Shrinkage TD (150°C)  92  0.9  %  Unrestrained @ 150°C/30 min

Contact Info

DuPont Teijin Films U.S. Limited Partnership 3600 Discovery Drive P.O. Box 411 Hopewell, VA 23860 USA Tel: (800) 635-4639 Fax: (804) 530-9867

Disclaimer

Note: These values are typical performance data for DuPont Teijin Films' polyester film; they are not intended to be used as design data. We believe this information is the best currently available on the subject. It is offered as a possible helpful suggestion in experimentation you may care to undertake along these lines. It is subject to revision as additional knowledge and experience is gained. DuPont Teijin Films makes no guarantee of results and assumes no obligation or liability whatsoever in connection with this information. This publication is not a license to operate under, or intended to suggest infringement of, any existing patents. CAUTION: Do not use in medical applications involving permanent implantation in the human body (DuPont Teijin Films Medical Policy). For other medical applications, see the Medical Caution Statement. DuPont Teijin Films accepts no liability for use of it's products in medical applications not reviewed and approved by DuPont Teijin Films or for product misuse. DuPont Teijin Films supplies products to an agreed specification and does not manufacture products designed specifically for medical end use. Melinex®, Mylar® and Melinex® STTM are registered trademarks of DuPont Teijin Films U.S. Limited Partnership. Teijin® and Tetoron® are registered trademarks of Teijin Limited used under license by DuPont Teijin Films U.S. Limited Partnership. Teonex® is a registered trademark of Teijin DuPont Films Japan Limited and is used under license by DuPont Teijin Films U.S. Limited Partnership.